Look like a perfect demonstration on how to ruin M390 steel?
-No any decarb protection when forging.
-No any annealing process after forging....
Hello, I'm not sure if the SNAFU is sold to me or someone else? I gave my E-mail above and I do have shipping address in the USA.
my paypal is : [email protected]
I'll take SNAFU please.
One of the best in this kind of rustic, traditional combined. You have such a amazing sense of artist sir.
Really awesome blade indeed! May I ask where do you live? The style and everything does looks familiar with Thailand...
I have been wanting David Sharp Loveless for years and this beauty just came up!
Would me take some if you don't mind :D
I don't always buy a book but when I do:
14 more to come next week tho!
From my experience both sharpen easily but M390 will hold an edge far better and also resist rust better too. Toughness wise, I never chipped or...
Definitely a killer piece from Tad!
Not sure if I should call this"persian" or not..
Stainless/High carbon San-Mai...
Yes, differential heat treating does result in differing hardness on each portion of the blade. The numbers are depend on steel, heat treat and...
There are several way to differential heat treat like using clay, torching spine, edge quench or torching just the edge etc. The main goal of...
Sound like you need some Pakismascus bowie...
San-Mai is a Japanese word mean "three parts" refer to the method making those blade which is forge welding 3 peices of steel (2 as jacket and 1...
Maraging steel? something like Aermet-340 should be super tough at decent hardness.
Tracker Dan Bloodshark used to sold for $1,500+ on secondary market.
CRK use Devin Thomas Damascus for long time before change to Chad Nichols Damascus several years ago. Both makers use AEB-L/304.