1. This site uses cookies. By continuing to use this site, you are agreeing to our use of cookies. Learn More.

  2. Click here to enter the drawing for your chance to win a Kizer 1034A1 Gingrich Bush Knife & Ka-Bar Dozier Folding Hunter, , Bladeforums.com swag or memberships!

    Be sure to read the rules before entering, then help us decide next week's giveaway by hitting the poll in that thread! Entries close at midnight, Saturday Sept 7!

    Once the entries close, we'll live stream the drawing on Sunday, Sept 8 at 5PM Eastern. Tune in to our YouTube channel TheRealBladeForums for a chance to win bonus prizes!

    Questions? Comments? Post in the discussion thread here

Food safe scale?

Discussion in 'Hammer & Tongs' started by EastCompassoKnivery, Jun 27, 2016.

  1. EastCompassoKnivery

    EastCompassoKnivery

    77
    Feb 26, 2014
    Hi! I'm looking in to making a Nakiri style knife soon and on this particular style of blade I find the black oxide scale left behind from heat treat looks rather wonderful, but is it food safe? Part of me thinks that it's not actually coming off into the food so it's fine but it's something j want to be sure on before I actually do it. Any info would be wonderful:) thanks!
     
  2. mete

    mete Gold Member Gold Member

    Jun 10, 2003
    The oxide will be porous and collect things that add flavors ,bacteria . In the old days when I was a kid we knew how to wash knives - hot water and detergent or soap .
     
  3. tim37a

    tim37a

    918
    May 18, 2010
    If you are planning to use it in a commercial kitchen, I don't think an inspector will accept it.
     
  4. Stacy E. Apelt - Bladesmith

    Stacy E. Apelt - Bladesmith ilmarinen - MODERATOR Moderator Knifemaker / Craftsman / Service Provider

    Aug 20, 2004
    It's been a while since my restaurant/kitchen days, but don't recall any inspector making a complaint about knives with the upper bevel in a rough finish. They do complain when any knife is left uncleaned.

    Many high end Japanese blades have a rough upper bevel. Some are pretty black. I know several chefs who have purchased such blades from me and other makers, and none have expressed any concern.

    As to your question, HT scale is iron oxide. It is not toxic. If it is actually scale, it will wear or flake off. If it is just the rough finish on the steel, it will hold up pretty well. I darken the upper bevel by soaking in FC and then finish the ha-ji.
     